Epoxy resin / inorganic accept rice composite material, have exceedingly good mechanical, heat-resisting, corrosion resistance and dimension stability, still have a lot of other and superior performance, wait for a domain to will show wider applied perspective in electronics, optical, mechanical, biology, medicine consequently. Epoxy resin base inorganic accept rice the development of composite material, reflected technology of advanced accept rice material the effective modified of current to the tradition product, it is changed for the function of epoxy resin and high-powered change open up a new capacious development way. Composite material has the rice of annulus oxygen accept that uses mixture law preparation Al2O3/ of rice of oxygen of annulus of TiO2/ of rice of oxygen of oxygen of annulus of accept rice CB/ , annulus of accept rice SiO2/ , accept, accept oxygen of annulus of BaTiO3/ of rice of annulus oxygen, accept, the research of epoxy resin of modified of particle of rice of accept of inorganic of near future industry, have new discovery and progress ceaselessly, expert choose should undertake introductory. Home is used mixed legal system to have in all composite material of epoxy resin of accept rice CB/ , studied different processing technique and CB add the effect that measures pair of material performance. Experimental result makes clear, with the composite material of pretreatment law preparation purer epoxy resin does not have too big change, reduce somewhat even; And use mechanical function has the composite material that joins law preparation directly to rise apparently, good when the function when adding a quantity to be 2 ％ , tensile strength, flexural strength, impact strength, rupture percentage elongation achieves 82MPa, 107MPa, 20.0kJ/m2 respectively, 3.03% , rose respectively than pure epoxy resin 32.3% , 10.3% , 88.7% , 39.6% ; Add the addition of the quantity as accept rice CB, the vitrification temperature of material also had very big rise, add a quantity to be when its 5% when vitrification temperature raised 20 ℃ , accept rice CB is controlled in 20nm and dispersive and even. Accept rice SiO2 belongs to material of three-dimensional accept rice by its measure namely accept rice particle. The expert says, the research that fastens to this an organic whole basically is centered on mechanical function and hot property, mixed legal system to have in all through solution composite material of epoxy resin of accept rice SiO2/ , after experimental result shows classics ultrasonic is handled, accept rice SiO2 is equably dispersedly with the 2nd form that collects voice in epoxy resin matrix, in the as dosage of accept rice SiO2 addition inside certain limits, the mechanical function of composite material increases gradually, it is when dosage 3% when reach great value, impact strength rises to 19.04kJ/m2 from the 8.5kJ/m2 of pure epoxy resin, tensile strength increases 50.78MPa from 38.95MPa, rupture percentage elongation from 2.17% rise 2.56% . In addition the heat-resisting function of composite material also gets ameliorative, it is when dosage of accept rice SiO2 3% when, its are initiative decompose temperature by pure resinous 270.2 ℃ raise 275.5 ℃ , increase to raise 281.8 ℃ for 5% when dosage. Accept rice TiO2 belongs to material of three-dimensional accept rice by its structure measure, as compound as EP have enhance the likelihood that increases pliable but strong. According to expert introduction, its consider to involve mechanical function, hot property and solidify kinetic. The expert studied the property of composite material of epoxy resin of fill of accept rice TiO2: Accept rice TiO2, watch chloric alcohol is joined below 60 ℃ base in epoxy resin, after classics ultrasonic is handled, join 1, 3 ― inferior 2 amine regard phenyl as solidify agent. Compare to the composite material photograph of epoxy resin with the TiO2 fill of micron dimension, more fatigue than the ― of meet an emergency of pure annulus oxygen intensity raised the composite material of accept rice fill 15% , the epoxy resin that compares micron fill is tall also; Fighting the side that blow besmear, the epoxy resin that accept rice TiO2 adds presents a remarkable result. The research that increases function of report of epoxy resin interpose to reduce interpose report loss as far as possible also has a story, accept rice particle is in hydro-thermal complex BaTiO3 the classics in acetone mixes with epoxy resin after supersonic processing, with second agent of 2 amine solidify makes its solidify, discover what accumulate content as human body of mix into of particle of BaTiO3 accept rice to increase, the dielectric constant of epoxy resin composite material is shown nonlinear increase. Still the expert uses the N-A12O3 of different content, accept rice particle and solidify agent (DDM2 amino 2 phenyl firedamp) mix even, be in its dispersedly equably in 90 ℃ epoxy resin (E-51, in 168) and solidify shapes. They basically studied N-A12O3, content is mixed to IP of the attrition inside system of epoxy resin composite material the influence that cuts modular amount, discovery becomes N-A12O3: Accept rice particle is 0.001 when ß-IP peak increases, and modular amount is fixed; When N-A12O3, value of accept rice particle is 0.01, 0.05 when ß-IP peak is slow reduce, but modular quantity is reduced very quickly; When N-A12O3, accept rice particle increases 0.1 when ß-IP peak is reduced significantly, modular quantity restores not to add the modular value of a quantity of the material when accept rice particle. The expert says, the affiliation of N-A12O3 of visible accept rice is right of epoxy resin inside the effect with chafe and cut modular quantity to rise very main.